Abstract This study evaluated how Er,Cr:YSGG laser, associated or not with 5% fluoride varnish, influences the surface roughness and volume loss of bovine root dentin submitted to erosive and/or abrasive wear. One hundred and twenty dentin specimens were divided into the groups: without preventive treatment (WPT), 5% fluoride varnish (FV); Er,Cr:YSGG laser irradiation (L), and varnish combined with laser (FV + L). The specimens (n = 10) were subdivided into: 1 = erosion (E); 2 = abrasion (A); and 3 = erosion followed by abrasion (E + A). The erosive solution used was a soft-drink (pH = 2.42 at 4ºC) applied in 5-min cycles twice a day for 10d. Abrasive wear involved brushing for 60s with an electric brush (1,600-oscillations/s) at a load of 2.0N. Surface roughness and volume loss were evaluated using a laser scanning confocal microscope. Roughness data were submitted to one-way ANOVA and Tukey post-hoc test. For volume loss, the Kruskal-Wallis and Dunn’s post-hoc tests were used (α = 5%). The lowest values of roughness were found in the control areas of all subgroups (p > 0.05). In the experimental area, the [(WPT) + (E+A)] subgroup had a significantly higher roughness (5.712 ± 0.163 μm 2 ) than the other subgroups (p < 0.05). The L and (FV + L) groups had statistically similar roughness, regardless of the type of wear. The (FV + L) group had the lowest volume loss, regardless of the type of wear performed: [(FV + L) + (E)] = 7.5%, [(FV + L) + (A) = 7.3%, and [(FV + L) + (E + A)] = 8.1%. The subgroup [(WPT) + (E + A)] had the highest volume loss (52.3%). The proposed treatments were effective in controlling dentin roughness. Laser irradiation can be an effective method to increase root dentin resistance after challenges and limit problems related to non-carious lesions.

This study evaluated the effect of surface sealant on the translucency of composite resin immersed in different solutions. The study involved the following materials: Charisma, Fortify and coffee, Coca-Cola®, tea and artificial saliva as solutions. Sixty-four specimens (n = 8) were manufactured and immersed in artificial saliva at 37 ± 1 °C. Samples were immersed in the solutions for three times a day and re-immersed in artificial saliva until the translucency readings. The measurements were carried out at nine times: T1 - 24 hours after specimen preparation, T2 - 24 hours after immersion in the solutions, T3 - 48 hours and T4 to T9 - 7, 14, 21, 30, 60 and 90 days, respectively, after immersion. The translucency values were measured using a JOUAN device. The results were subjected to ANOVA and Tukey's test at 5%. The surface sealant was not able to protect the composite resin against staining, the coffee showed the strongest staining action, followed by tea and regarding immersion time, a significant alteration was noted in the translucency of composite resin after 21 days.

The aim of this in vitro study was to assess the effect of different fluoride-containing mouthrinses on the translucence of resin-modified glass ionomer cements, as a function of the restorative material used, the fluoride-containing solution employed and the time of immersion. Disks were prepared (10 mm × 2 mm) with the modified glass ionomer cements Vitremer (3M) and Fuji II LC (GC Co.), and immersed in three fluoride-containing solutions: Fluordent Reach (Johnson & Johnson), Fluorgard (Colgate-Palmolive) and Oral B (Gillette do Brasil Ltda). Translucence was measured with electrophoresis equipment (JOUAN) after different immersion times. The results obtained were submitted to ANOVA and Tukey's test, and a statistically significant decrease was observed in the translucence of the materials after immersion in the fluoride-containing solutions. Fuji II LC demonstrated the lowest alteration in translucence, independently of the solution employed. Fluorgard was the fluoride-containing mouthrinse that promoted the highest alteration. It can be concluded that the fluoride-containing mouthrinses influenced the translucence of the resin-modified glass ionomer cements.